K10 Tungsten Carbide Rod Blanks with 6% Cobalt , High Hardness tungsten carbide metal

K10 Tungsten Carbide Rod Blanks with 6% Cobalt, Hardness 93.5 - 93.8 HRA

Description: 

Cemented carbide essentially consists of two main components: hard metal tungsten carbide (WC) and binding agent Co. Carbide contributes to high hardness property in a most important degree for hard metal WC, while cobalt maintains its relative high toughness at the high level of hardness. With Hot Isostatic Pressing sintering technique, cemented carbide material is fully consolidated by simultaneous application of heat and pressure, producing a close-to-full-density state. Consequently, the technique greatly optimizes rod’s quality, being more stable and reliable. 

- ISO Range: K10

- with 94% tungsten carbide, 6% cobalt 

- Made of 0.4 micron ultrafine TC powder

- Hardness: 93.5-93.8 HRA

- Bending strength: >3200 MPa

- Density: 14.8 g/cm3

- As sintered
                                            
- Dimension: unground fixed length bar in metric size

Specifications:

Solid rods- cut to length(Metric):

D	Tolerance of D	Length	D	Tolerance of D	Length
mm	(mm)	mm	mm	(mm)	mm
3.0	+0.2/+0.4	38.5	8.0	+0.2/+0.4	100
3.0	+0.2/+0.4	50	8.0	+0.2/+0.4	More»Our other products High Hardness Cut to K30 - K40 Tungsten C 3800 MPa Sintering C 330 mm Tungsten Carb YG8 Six Facet Anvil CO 10% Ground Cement 99.8% Purity Raw WC K10 Tungsten Carbide Tips：This page [K10 Tungsten Carbide Rod Blanks with 6% Cobalt , High Hardness tungsten carbide metal] infomation provided by [Jiangsu Hetian Technological Material Co., Ltd.] ,the enterprise is responsible for the authenticity, accuracy and validity of the information content. www.tradeleo.com do not assume any guarantee of joint and several liability. A safe way to suggest that the two sides trade, to ensure the interests of both sides. [ Sell search ]  [ Favorites ]  [ Tell friends ]  [ Print ]  [ Close ]   HomeSite | About us | Contact Us | Agreement | Copyright | Sitemap | Spread | Guestbook | RSS Feed © 2000-2015 tradeleo.com All Rights Reserved | Without www.tradeleo.com written permission,Do not copy this site all information works and business information.